Effect of multi-layer applications of self-etch universal bonding agents on the adhesion of resin composite to enamel

Vitaliano Gomes Araújo-Neto; Francisbênia Alves Silvestre; Diego Lomonaco; Salvatore Sauro; Victor Pinheiro Feitosa; Marcelo Giannini

doi:10.1007/s10266-024-00970-w

To evaluate the effect of adhesive coats application on the enamel microtensile bond strength (µTBS) of universal adhesives, morphological etching pattern and their chemical interaction with hydroxyapatite (HA). Two universal adhesives were investigated: Scotchbond Universal (SBU, 3 M) and Prime&Bond Universal (PBU, Dentsply). The adhesives were applied in self-etching mode on bovine enamel (n = 8) in one (1L), two (2L) or three coats (3L) and light-cured as per manufacturers' instructions. As controls adhesives were applied to etched enamel (H3PO4-37% phosphoric acid). Bonded specimens were cut into sticks that were stored in deionized water for 24 h or 6 months prior to µTBS testing. Two-way ANOVA and Tukey's test were used for statistical analysis of bond strength with α = 5%. For morphological SEM analysis, enamel surfaces were treated as aforementioned and immediately rinsed with acetone. The intensity of monomer-calcium salt formation from each treatment was measured via infrared spectroscopy (ATR-FTIR). All treatments presented no significant reduction on µTBS after aging (p > 0.05). However, SBU attained highest µTBS when applied in 3L. PBU showed higher µTBS when applied to H3PO4 etched enamel than 1L or 2L. Etching pattern was enhanced by 3L application, particularly with PBU. Chemical interaction was notably higher for SBU than PBU, with no relevant differences with more layers or prior H3PO4-etching. The application of three adhesive coats of universal adhesives in self-etch mode using may enhance the bonding performance and etching pattern to enamel, surpassing the H3PO4-etched enamel bond for SBU. The chemical interaction with calcium from enamel is not affected by number of coats or prior phosphoric acid etching.To evaluate the effect of adhesive coats application on the enamel microtensile bond strength (µTBS) of universal adhesives, morphological etching pattern and their chemical interaction with hydroxyapatite (HA). Two universal adhesives were investigated: Scotchbond Universal (SBU, 3 M) and Prime&Bond Universal (PBU, Dentsply). The adhesives were applied in self-etching mode on bovine enamel (n = 8) in one (1L), two (2L) or three coats (3L) and light-cured as per manufacturers' instructions. As controls adhesives were applied to etched enamel (H3PO4-37% phosphoric acid). Bonded specimens were cut into sticks that were stored in deionized water for 24 h or 6 months prior to µTBS testing. Two-way ANOVA and Tukey's test were used for statistical analysis of bond strength with α = 5%. For morphological SEM analysis, enamel surfaces were treated as aforementioned and immediately rinsed with acetone. The intensity of monomer-calcium salt formation from each treatment was measured via infrared spectroscopy (ATR-FTIR). All treatments presented no significant reduction on µTBS after aging (p > 0.05). However, SBU attained highest µTBS when applied in 3L. PBU showed higher µTBS when applied to H3PO4 etched enamel than 1L or 2L. Etching pattern was enhanced by 3L application, particularly with PBU. Chemical interaction was notably higher for SBU than PBU, with no relevant differences with more layers or prior H3PO4-etching. The application of three adhesive coats of universal adhesives in self-etch mode using may enhance the bonding performance and etching pattern to enamel, surpassing the H3PO4-etched enamel bond for SBU. The chemical interaction with calcium from enamel is not affected by number of coats or prior phosphoric acid etching.

Effect of multi-layer applications of self-etch universal bonding agents on the adhesion of resin composite to enamel

View Online

Abstract

Details

Metrics