Relationship between nanoleakage and microtensile bond strength at the resin-dentin interface
Operative dentistry, Vol.28(1), pp.60-66
01/2003
PMID: 12540120
Abstract
To evaluate the correlation between microtensile dentin bond strength (microTBS) and silver ion penetration, two total-etch 3-step and one self-etch 2-step system were investigated. OptiBond FL adhesive was applied to flat occlusal dentin on six non-carious human molars, and a resin composite "crown" was formed in 2 mm increments. After 24-hour water storage, the teeth were sectioned with a low-speed diamond saw to obtain four-square sticks (approximately 2 mm X 2 mm) per tooth. Cylindrical tensile test specimens were formed with an 0.5 mm2 cross-sectional area. Nail varnish was applied to the dentin within 0.5-1.0 mm of the interface before immersing in 50% silver nitrate for 15 minutes. Following silver fixation, tensile testing was performed in a Zwick UTM at 1 mm/minute using a passive gripping fixture to obtain 72-hour microTBS [23.9 MPa]. The percentage area of silver penetration was measured on debonded specimens using light microscopy and Image-Pro Plus Software [89%]. The procedures were repeated using Scotchbond Multi-Purpose Plus [microTBS = 27.8 MPa; nanoleakage = 67%] and Clearfil SE bond [microTBS = 36 MPa; nanoleakage = 55%]. No significant correlation between microtensile bond strength and nanoleakage was found for all systems. A weak-to-moderate negative relationship was found between microTBS and nanoleakage for OptiBond FL (Spearman r = -0.3844). No correlation was found for the remaining adhesive systems. The correlation between these two common laboratory measurements appears to be adhesive-system dependent.
Details
- Title: Subtitle
- Relationship between nanoleakage and microtensile bond strength at the resin-dentin interface
- Creators
- Sandra Guzmán-Armstrong - College of Dentistry, Department of Operative Dentistry, University of Iowa, Iowa City, IA 52242, USA. sandra-guzman-armstrong@uiowa.eduSteven R ArmstrongFang Qian
- Resource Type
- Journal article
- Publication Details
- Operative dentistry, Vol.28(1), pp.60-66
- Publisher
- United States
- PMID
- 12540120
- ISSN
- 0361-7734
- eISSN
- 1559-2863
- Language
- English
- Date published
- 01/2003
- Academic Unit
- Preventive and Community Dentistry; Operative Dentistry; Dental Research
- Record Identifier
- 9984065987702771
Metrics
30 Record Views